移动设备用 柔性基板材料「FELIOS」系列 : 型号

精确检索
Found 121 matches /121件中
每页的件数
件
仅限已选择的产品编号
选项 型号 目录 /
数据表		 系列/类型 Copper Foil Type Copper Foil Part No. Copper Foil Thickness
(µm) 		Fiim Thickness
(µm) 		Total products thickness
(µm) 		Peel Strength.90°:JIS C 6471.A
(mm) 		Peel Strength.90°:JIS C 6471.260℃ Solder 5sec
(mm) 		Dimensional Stability.MD:IPC-TM-650.After Etching
(%) 		Dimensional Stability.TD:IPC-TM-650.After Etching
(%) 		Dimensional Stability.MD:IPC-TM-650.Ｅ-0.5/150
(%) 		Dimensional Stability.TD:IPC-TM-650.Ｅ-0.5/150
(%) 		Soldering Resistance:JIS C 6471.A
(°C) 		Soldering Resistance:JIS C 6471.C-96/40/90
(°C) 		MIT Test:JIS C 6471.0.38R×4.9N,MD MIT Test:JIS C 6471.0.38R×4.9N,TD Tensile　Modulus:IPC-TM-650
(GPa) 		Coefficient of Thermal Expansion.MD:TMA　100℃→250℃，
5℃/min
(ppm/K) 		Coefficient of Thermal Expansion.TD:TMA　100℃→250℃，
5℃/min
(ppm/K) 		Dielectric Constant at 1MHz:IPC-TM-650　2.5.5.5.A Dielectric Constant at 2GHz:IPC-TM-650　2.5.5.5.A Dielectric Constant at 10GHz:Cavity resonance.A Dissipation Factor at 1MHz:IPC-TM-650　2.5.5.5.A Dissipation Factor at 2GHz:IPC-TM-650　2.5.5.5.A Dissipation Factor at 10GHz:Cavity resonance.A Insulation resistance:JIS C 6471.A
(Ω)		 Insulation resistance:JIS C 6471.C-96/40/90
(Ω)		 Water absorption.IPC-TM-650:JIS C 6471.D-24/23
(%) 		Water absorption:JIS C 6471.D-24/23
(%) 		Moisture Absorption.IPC-TM-650:C-24/23/50
(%) 		Tg:DMA.A
(°C) 		Flammability:UL 94.A+E-168/70 * These are observed data, not guaranteed performance.
The test method of above item is determined according to Panasonic internal standard.		 Glass transition temp.(Tg) :TMA(Ad)
(°C) 		Glass transition temp.(Tg) :DMA
Measurement in tensile mode(Ad)
(°C) 		CTE:α1,X-axis,IPC-TM-650 2.4.24
(ppm/°C)		 CTE:α1,Y-axis,IPC-TM-650 2.4.24
(ppm/°C)		 CTE:α1,Z-axis,IPC-TM-650 2.4.24
(ppm/°C)		 CTE:α2,Z-axis,IPC-TM-650 2.4.24
(ppm/°C)		 Volume resistivity:IPC-TM-650 2.5.17.1,C-96/35/90
(MΩ·cm)		 Dielectric constant(Dk)@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 (Ad) Dissipation factor(Df )@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 (Ad) Water absorption:IPC-TM-650 2.6.2.1,D-24/23
(%)		 Peel strength,1oz:IPC-TM-650 2.4.8
(kN/m (lb/inch))		 Flammability:UL,A+E-168/70 The sample thickness *1 Condition: C-96/20/65, Unit : MΩ·m *2 Condition: E-24/50+D-24/23 *3 Measured by R-FR10/R-F775 25μm/ R-FR10 construction
R-F700S_12EC_18-25-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 18 25 43 0.8 0.8 0.058 0.021 0.092 0.064 310 290 255 250 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_13EC_12-25-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 12 25 37 0.75 0.75 0.036 0.01 0.082 -0.041 310 290 300 280 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_22EC_18-50-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 18 50 68 0.8 0.8 0.064 0.029 0.108 0.073 310 290 118 83 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_23EC_12-50-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 12 50 62 0.75 0.75 0.04 -0.039 0.089 -0.039 310 290 84 61 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_32EC_18-75-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 18 75 93 0.8 0.8 0.0265 0.0167 0.0717 0.0582 310 290 28 18 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_33EC_12-75-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 12 75 87 0.75 0.75 0.033 0.002 0.072 0.017 310 290 28 18 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_43EC_12-100-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 12 100 112 0.75 0.75 -0.018 -0.036 0.009 -0.029 310 290 10 8 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_A3EC_12-125-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 12 125 137 0.75 0.75 0.0278 0.0156 0.077 0.0375 310 290 4 4 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F700S_B3EC_12-150-0(ED)
 R-F700S (LCP* Single-sided copper clad) ED TP4-S 12 150 162 0.75 0.75 0.0424 0.0285 0.0973 0.0713 310 290 3 3 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_12EC_18-25-18(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 18 25 61 0.8 0.8 0.024 -0.006 0.07 0.015 310 290 220 190 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_13EC_12-25-12(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 12 25 49 0.75 0.75 0.019 -0.021 0.054 -0.01 310 290 280 290 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_14EC_9-25-9(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 9 25 43 0.65 0.65 0.032 0.001 0.088 0.036 310 290 70 60 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_22EC_18-50-18(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 18 50 86 0.8 0.8 0.016 -0.038 0.05 -0.035 310 290 110 100 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_23EC_12-50-12(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 12 50 74 0.75 0.75 -0.004 -0.058 -0.002 -0.073 310 290 85 70 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_24EC_9-50-9(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 9 50 68 0.8 0.8 0.007 -0.053 0.04 -0.056 310 290 60 50 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_32EC_18-75-18(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 18 75 111 0.8 0.8 0.064 0.042 0.121 0.094 310 290 32 28 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_33EC_12-75-12(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 12 75 99 0.75 0.75 0.021 0.006 0.028 0.004 310 290 22 16 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_34EC_9-75-9(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 9 75 93 0.65 0.65 -0.003 0.017 0.045 0.054 310 290 20 15 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_42EC_18-100-18(ED
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 18 100 136 0.8 0.8 0.007 -0.002 0.034 0.021 310 290 16 12 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_43EC_12-100-12(ED
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 12 100 124 0.75 0.75 -0.016 -0.049 0.009 -0.052 310 290 11 8 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_44EC_9-100-9(ED)
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 9 100 118 0.65 0.65 0.021 0.02 0.06 0.044 310 290 8 8 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_A2EC_18-125-18(ED
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 18 125 161 0.75 0.75 0.0463 0.0354 0.0996 0.0765 310 290 6 6 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_A3EC_12-125-12(ED
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 12 125 149 0.75 0.75 0.02 -0.005 0.067 0.035 310 290 4 4 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_B2EC_18-150-18(ED
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 18 150 186 0.75 0.75 0.023 0.028 0.067 0.078 310 290 3 3 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F705S_B3EC_12-150-12(ED
 R-F705S (LCP* Double-sided copper clad) ED TP4-S 12 150 174 0.75 0.75 0.0301 0.0102 0.0821 0.0762 310 290 3 3 4.5 18 18 - - 3.3 - - 0.002 ＞1.0×10^14 ＞1.0×10^14 - 0.04 - - VTM-0 - - - - - - - - - - - - - - - - -
R-F770_10RB_70-25-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 70 25 95 2.5 2.5 -0.0277 0.0247 -0.0597 -0.003 330 260 33 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_11RB_35-25-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 35 25 60 1.6 1.6 0.006 -0.007 -0.036 -0.056 330 260 90 130 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_12EV_18-25-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 18 25 43 1.5 1.5 -0.0078 0.024 -0.0378 0.0021 330 260 180 170 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_12RB_18-25-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 18 25 43 1.5 1.5 -0.014 -0.013 -0.055 -0.057 330 260 180 200 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_13EV_12-25-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 12 25 37 1.5 1.5 0.019 0.008 0.009 0.001 330 260 230 220 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_13RX_12-25-0(RA)
 R-F770 (Single-sided copper clad) RA BHYX-T 12 25 37 1.5 1.5 -0.002 0.025 -0.02 -0.011 330 260 270 290 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_14EV_9-25-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 9 25 34 1.3 1.3 -0.003 0.023 -0.026 0.003 330 260 130 94 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_14RN_9-25-0(RA)
 R-F770 (Single-sided copper clad) RA BHY-HA-V2 9 25 34 1.3 1.3 -0.0127 -0.0022 -0.0425 -0.0255 330 260 340 340 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_16ES_6-25-0(ED)
 R-F770 (Single-sided copper clad) ED SEED 6 25 31 1 1 -0.0258 -0.0103 -0.0579 -0.0345 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_1PEL_2-25-0(ED)
 R-F770 (Single-sided copper clad) ED MT18FL 2 25 27 1.3 1.3 -0.0356 -0.0037 -0.0497 -0.0215 330 260 120 120 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_21RB_35-50-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 35 50 85 2.5 2.5 0.009 0.013 -0.0175 -0.0438 330 260 42 54 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_22EV_18-50-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 18 50 68 1.7 1.7 0.009 0.02 0.0082 0.013 330 260 35 35 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_22RB_18-50-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 18 50 68 1.5 1.5 -0.004 -0.01 -0.047 -0.046 330 260 60 60 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_23EV_12-50-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 12 50 62 1.6 1.6 0.011 0.009 -0.001 -0.009 330 260 40 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_23RX_12-50-0(RA)
 R-F770 (Single-sided copper clad) RA BHYX-T 12 50 62 1.5 1.5 -0.002 0.038 -0.031 0.001 330 260 40 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_26ES_6-50-0(ED)
 R-F770 (Single-sided copper clad) ED SEED 6 50 56 1 1 0.00050 0.0171 -0.0377 -0.0158 330 260 40 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_27RN_105-50-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 105 50 155 3 3 -0.0154 -0.0278 -0.0621 -0.0807 330 260 24 28 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_30RB_70-75-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 70 75 145 2.5 2.5 -0.0185 -0.00050 -0.0688 -0.0459 330 250 19 20 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_32EV_18-75-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 18 75 73 1.5 1.5 -0.008 -0.0058 -0.0304 -0.0328 330 250 15 18 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_33EV_12-75-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 12 75 87 1.5 1.5 -0.003 -0.0015 -0.0333 -0.0337 330 250 16 15 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_33RX_12-75-0(RA)
 R-F770 (Single-sided copper clad) RA BHYX-T 12 75 87 1.5 1.5 0.0102 0.0175 -0.0334 -0.0242 330 250 22 33 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_41EM_35-100-0(ED)
 R-F770 (Single-sided copper clad) ED T4M-HDR 35 100 135 3 3 -0.0218 -0.0222 -0.056 -0.0556 330 250 12 12 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_42EV_18-100-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 18 100 118 2.6 2.6 -0.0088 -0.0085 -0.0381 -0.038 330 250 7 9 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_42RB_18-100-0(RA)
 R-F770 (Single-sided copper clad) RA BHY 18 100 118 2 2 -0.006 -0.0063 -0.0283 -0.0251 330 250 14 13 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F770_43EV_12-100-0(ED)
 R-F770 (Single-sided copper clad) ED VLP 12 100 112 2.4 2.4 -0.012 -0.014 -0.029 -0.03 330 250 10 10 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - ＞1.0×10^14 ＞1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -