Non-silicone thermosetting insulation film with high heat resistance and environmental stability.
A pliable and stretchable substrate follows 3D shapes that cannot be achieved with conventional flexible substrates.
Can be the foundation for many new innovative applications for stretchable electronics.
- Part Number
MUAS13111AA
- Application
- Detailed use
・Healthcare
・Wearable
・Wearable
Devices in printed electronics applications such as wearable, healthcare, medical, automotive, energy harvesting, aerospace, etc.
Properties
Good elongation
Low hysteresis
High temperature resistance
Concept
BEYOLEX is an unique insulation material based on a proprietary, thermoset, non-silicone polymer system which provides softness, conformability, high-temperature resistance, and compatibility with a wide variety of functional inks and pastes, contributes to the creation of new innovative stretchable electronics.
Video
Demonstrator Video (Production cooperation: Printed Electronics Ltd.)
LED: Wiring does not break when bent or stretched and returns to its original state.
NFC: In addition to stretching and shrinking, immersion in water does not cause functional problems.
General properties
Item | Test method *¹ | Unit | BEYOLEX MUAS13111AA |
|
Elongation | ASTM D822 | Initial | % | 200 < |
Aft. High Temp. and High Humid. test *² | 200 < | |||
Aft. Heat cycle *³ | 200 < | |||
Modulus @50% strain | ASTM D822 | Initial | MPa | < 2.5 |
Aft. High Temp. and High Humid. test | < 2.5 | |||
Aft. Heat cycle | < 2.5 | |||
Hysteresis | Panasonic Original | Initial | % | < 0.1 |
Aft. High Temp. and High Humid. test | < 0.1 | |||
Aft. Heat cycle | < 0.1 | |||
Heat resistance | TG/DTA (@Air) 5% weight loss | °C | 302 | |
Breakdown voltage | IEC 60243-1 | KV/mm | 98 | |
Dielectric constant(Dk) | IPC TM650 2.5.5.10 | @10GHz / @2GHz | – | 2.8 / 3.3 |
Dissipation factor(Df) | @10GHz / @2GHz | – | 0.052 / 0.073 | |
Transparency | ISO 13468-1 | % | > 90 | |
Stretch cycle | 50% stretch | cycle | > 10000 |
*1 Measurement are compliant with the standards other than Panasonic’s original test.
*2 Test Condition: 85°C/ 85%RH/ 1000h
*3 Test Condition: -55°C(5min) ↔ 125°C(5min)/ 1000cyc
The above data are typical values and not guaranteed values.