R-FR10 : 移动设备用 柔性基板材料「FELIOS」系列

产品名
移动设备用 柔性基板材料「FELIOS」系列

系列/类型
R-FR10 (FRCC)

型号
R-FR10

放大
一张照片：R-FR10
项目 内容
Glass transition temp.(Tg) :TMA(Ad) (°C) 190
Glass transition temp.(Tg) :DMA
Measurement in tensile mode(Ad) (°C)		 210
CTE:α1,X-axis,IPC-TM-650 2.4.24 (ppm/°C) 80(Ad)
CTE:α1,Y-axis,IPC-TM-650 2.4.24 (ppm/°C) 80(Ad)
CTE:α1,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) 80(Ad)
CTE:α2,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) 580(Ad)
Volume resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ·cm) 1 x 10<sup>8</sup> *2
Dielectric constant(Dk)@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 (Ad) 3
Dissipation factor(Df )@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 (Ad) 0.019
Water absorption:IPC-TM-650 2.6.2.1,D-24/23 (%) 1.2 *4
Peel strength,1oz:IPC-TM-650 2.4.8 (kN/m (lb/inch)) 0.8(4.6)
(ED:12μm)
Flammability:UL,A+E-168/70 94VTM-0 *5
The sample thickness 0.032mm
(Cu:12μm, PI:5μm,Ad:15μm)
*1 Condition: C-96/20/65, Unit : MΩ·m -
*2 Condition: E-24/50+D-24/23 -
*3 Measured by R-FR10/R-F775 25μm/ R-FR10 construction -
Copper Foil Type -
Copper Foil Part No. -
Copper Foil Thickness (µm) -
Fiim Thickness (µm) -
Total products thickness (µm) -
Peel Strength.90°:JIS C 6471.A (mm) -
Peel Strength.90°:JIS C 6471.260℃ Solder 5sec (mm) -
Dimensional Stability.MD:IPC-TM-650.After Etching (%) -
Dimensional Stability.TD:IPC-TM-650.After Etching (%) -
Dimensional Stability.MD:IPC-TM-650.Ｅ-0.5/150 (%) -
Dimensional Stability.TD:IPC-TM-650.Ｅ-0.5/150 (%) -
Soldering Resistance:JIS C 6471.A (°C) -
Soldering Resistance:JIS C 6471.C-96/40/90 (°C) -
MIT Test:JIS C 6471.0.38R×4.9N,MD -
MIT Test:JIS C 6471.0.38R×4.9N,TD -
Tensile　Modulus:IPC-TM-650 (GPa) -
Coefficient of Thermal Expansion.MD:TMA　100℃→250℃，
5℃/min (ppm/K)		 -
Coefficient of Thermal Expansion.TD:TMA　100℃→250℃，
5℃/min (ppm/K)		 -
Dielectric Constant at 1MHz:IPC-TM-650　2.5.5.5.A -
Dielectric Constant at 2GHz:IPC-TM-650　2.5.5.5.A -
Dielectric Constant at 10GHz:Cavity resonance.A -
Dissipation Factor at 1MHz:IPC-TM-650　2.5.5.5.A -
Dissipation Factor at 2GHz:IPC-TM-650　2.5.5.5.A -
Dissipation Factor at 10GHz:Cavity resonance.A -
Insulation resistance:JIS C 6471.A (Ω) -
Insulation resistance:JIS C 6471.C-96/40/90 (Ω) -
Water absorption.IPC-TM-650:JIS C 6471.D-24/23 (%) -
Water absorption:JIS C 6471.D-24/23 (%) -
Moisture Absorption.IPC-TM-650:C-24/23/50 (%) -
Tg:DMA.A (°C) -
Flammability:UL 94.A+E-168/70 -
* These are observed data, not guaranteed performance.
The test method of above item is determined according to Panasonic internal standard.		 -